مقاله جوشكاري Electrical contact resistance effect on resistance spot welding

مقاله جوشكاري با عنوان : Electrical contact resistance effect on resistance spot welding

P.S. Wei a,., T.H. Wub

چكيده :

The effects of local electrical contact resistance on transport variables, cooling rate, solute distribution,
and nugget shape after solidification responsible for microstructure of the fusion zone during resistance
spot welding are realistically and systematically investigated. The model accounts for electromagnetic
force, heat generation and contact resistances at the faying surface and electrode–workpiece interfaces
and bulk resistance in workpieces. Contact resistances are composed of film and constriction resistances,
as functions of hardness, temperature, electrode force and surface condition. The computed results show
that the bulk dynamic electrical resistance cannot reliably reflect transport processes and nugget shape,
unless the local constriction resistance and electric current density are known. Regardless of high film
resistance, nugget growth and transport processes are independent of film resistance due to delayed
response time of local electric current in the early stage. A decrease in constriction resistance, however,
delays nugget formation, enhances convection and solute mixing, and changes circulation direction of the
stronger convection cell during cooling period.

مقاله جوشكاري Effects of Welding Parameters and Surface Pretreatments on Resistance Spot Welding of AZ31B Mg Alloy

مقاله جوشكاري با عنوان :

Effects of Welding Parameters and Surface Pretreatments on Resistance
Spot Welding of AZ31B Mg Alloy

Shiquan Zhou1, Lei Liu2,3, Jae Pil Jung4,*, Mok-Young Lee5, and Y. Norman Zhou3

چكيده :

The resistance spot weldability of AZ31B magnesium alloy using AC (alternating current) was investigated
in this paper. The surfaces of sheet coupons were prepared by acetone cleaning (as-received) and some coupons
were also cleaned with chromic acid (H2Cr2O7) after acetone cleaning (acid-cleaned). The surfaces of the
as-received AZ31B sheets consisted of MgO, Mg(OH)2, and MgCO3. The extent and thickness of the surface
oxide/reaction layer of the sheets varied according to the fabrication process of the sheets, and resulted in
different contact resistance. Effects of welding current and weld time were investigated while the electrode
force was kept constant. The results indicated that the as-received sheets produced expulsion both at the
faying surface and at the work piece/electrode interface due to high contact resistance. Diluted chromic acid
cleaning reduced contact resistance and produced good weld quality. Increasing the welding current and weld
time enhanced not only the nugget size and joint strength, but also increased indentation on the weld surfaces.
A weld lobe was established considering the minimum joint strength, weld expulsion, and surface indentation
based on a relevant American Welding Society Standard.

بررسي اثر زمان و جريان جوشكاري بر ابعاد دكمه جوش در فرآيند جوشكاري مقاومتي نقطه اي

شبيه سازي تنشهاي پسماند جوشي در جوشكاري مقاومتي نقطهاي ورقهاي فولادي

تاثير متغيرهاي فرآيندجوشكاري مقاومتي نقطه اي بر استحكام نهايي ورق فولادي St12

در اين مقاله تاثير برخي از متغيرهاي جوشكاري مقاومتي نقطهاي مانند زمان، شدت جريان و فشار الكترودها بر استحكام برشي(ماكزيمم نيرو) نقطه جوشها در فولاد St12 به ضخامت 0/9mm مورد بررسي قرار گرفته است. ظرفيت دستگاه جوش نقطهاي 120KVA و الكترودها از جنس مس- كرم با قطر تماس 5mm بودند. ورقها تحت شرايط مختلف جريان، زمان و فشار با استفاده از تكنيك طراحي آزمايشات جوشكاري شدند و سپس تحت آزمايش استاندارد كشش –برش قرار گرفتند تا تاثير متغيرهاي فوق بر استحكام برشي جوشها مشخص گردد. با استفاده از نتايج آزمايشات ، به روش رويه پاسخ و به كمك نرمافزار Minitab ، مدل رياضي درجه دومي جهت پيشبيني تاثير متغيرهاي مذكور بر استحكام برشي بدست آورده شد. پس از مدلسازي با استناد به تحليل واريانس (ANOVA) و سطح اطمينان 95 درصد، انطباق اين مدل با فرآيند واقعي بررسي گرديد و اعتبار مدل پيشنهادي به كمك آزمون فرضيات آماري صحه گذاري و تاييد شد. نتايج مدل سازي نشان داد كه افزايش جريان و زمان باعث افزايش و سپس كاهش استحكام برشي گرديد درحاليكه افزايش فشار الكترودها منجر به كاهش استحكام برشي شد.

بررسي تغييرات ريزساختاري و قطر دكمه جوش مقاومتي نقطه اي فولادTRIP بعد از عمليات تمپر به كمك پارامترهاي جوشكاري مقاومتي

در اين تحقيق تغييرات ريزساختاري و قطر دكمه جوش فولاد TRIP بعد از عمليات تمپر جوش، مورد بررسي قرار گرفت. در اين بررسي برروي نقطه جوش هاي ورق اين نوع فولاد به كمك پارامترهاي جريان و زمان جوشكاري در جرياني پايينتر از جريان جوش اصلي و در سه زمان تمپر به ترتيب پايين، متوسط و بالاي زمان جوش اصلي، عمليات حرارتي تمپر انجام گرفت. مشخص شد كه در جريان و زمان هاي تمپر انتخاب شده، ريزساختار مارتنزيتي ناحيه جوش، به مارتنزيت تمپر شده و فريت تبديل مي شود كه با افزايش زمان تمپر، تجزيه مارتنزيت بيشتر انجام مي گردد. همچنين با اعمال سيكل هاي تمپر قطر دكمه جوش افزايش چنداني را نشان نمي دهد كه نشان دهنده يك نوع عمليات حرارتي بدون ذوب مجدد است